| General | ||||
|
Availability 1
|
|
|||
|
Uses
|
|
|||
|
Appearance
|
|
|||
|
Form(s)
|
|
|||
|
Processing Method
|
|
|||
|
Revision Date
|
|
|||
| Physical |
Typical Value
|
Unit
|
Test Based On
|
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
13
|
g/10 min
|
ASTM D1238 |
|
Density
|
0.9
|
g/cm3
|
ExxonMobil Method |
| Mechanical |
Typical Value
|
Unit
|
Test Based On
|
|
Tensile Strength at Yield (51 mm/min)
|
35.2
|
MPa
|
ASTM D638 |
|
Tensile Stress at Yield
|
33.4
|
MPa
|
ISO 527-2/50 |
|
Elongation at Yield (51 mm/min)
|
9.4
|
%
|
ASTM D638 |
|
Tensile Strain at Yield
|
7.1
|
%
|
ISO 527-2/50 |
|
Tensile Modulus - Chord
|
1580
|
MPa
|
ISO 527-2/1 |
|
Flexural Modulus - 1% Secant
|
|||
|
1.3 mm/min
|
1500
|
MPa
|
ASTM D790A |
|
13 mm/min
|
1770
|
MPa
|
ASTM D790B |
|
Flexural Modulus (2.0 mm/min)
|
1430
|
MPa
|
ISO 178 |
| Impact |
Typical Value
|
Unit
|
Test Based On
|
|
Notched Izod Impact (23°C)
|
22
|
J/m
|
ASTM D256A |
|
Notched Izod Impact
Strength (23°C)
|
3.1
|
kJ/m2
|
ISO 180/1A |
|
Charpy Notched Impact
Strength (23°C)
|
2.2
|
kJ/m2
|
ISO 179/1eA |
|
Gardner Impact (23°C, 3.18 mm, Geometry GC)
|
9.73
|
J
|
ASTM D5420 |
| Thermal |
Typical Value
|
Unit
|
Test Based On
|
|
Heat Deflection Temperature (1.80
MPa)
|
52.0
|
°C
|
ISO 75-2/Af |
|
Heat Deflection Temperature (0.45
MPa)
|
80.6
|
°C
|
ISO 75-2/Bf |
|
Deflection Temperature Under Load
(DTUL) at 66psi - Unannealed
|
92.4
|
°C
|
ASTM D648 |
|
DTUL @ 66psi - Annealed
|
114
|
°C
|
ASTM D648 |
| Hardness |
Typical Value
|
|
Test Based On
|
|
Rockwell Hardness
|
107
|
|
ASTM D785 |
|
Shore Hardness (15 sec)
|
67
|
|
ISO 868 |
| Legal Statement | |||
|
Contact your ExxonMobil Chemical Customer
Service Representative for potential food contact application compliance (e.g.
FDA, EU, HPFB).
This product, including the product name, shall not be used or tested in any medical application without the prior written acknowledgement of ExxonMobil Chemical as to the intended use. |
|||